HDPE Textured Geomembrane For Enhanced Impermeability And Environmental Protection
Product Introduction
Cylindrical point rough geomembrane is a type of geosynthetic material used in civil engineering whose surface is designed with special column points or textures to increase friction and adhesion with soil or other materials.
Product Properties
1. Enhanced coefficient of friction: The column point design provides a higher coefficient of friction, helping to prevent sliding of geomemes in slope or vertical applications.
2. Good impermeability: It maintains the excellent impermeability of HDPE geomembrane and effectively prevents the penetration of water and pollutants.
3. Chemical corrosion resistance: can resist the erosion of a variety of chemical substances, suitable for use in a variety of environmental conditions.
4. Resistance to environmental stress cracking: Excellent resistance to environmental stress cracking, able to maintain stability in harsh environments.
5. Temperature adaptability: It has good heat resistance and cold resistance and can be used in a wide temperature range.
Product Application
1. Slope engineering: Especially suitable for slope seepage prevention projects that need to enhance stability.
2. Landfill: used for slope anti-slip and anti-seepage of landfill to improve the safety and environmental protection of the project.
3. Tailings pond: used in the seepage prevention and stabilization project of tailings pond to prevent the leakage of harmful substances.
4. DAMS and reservoirs: Used for seepage prevention and reinforcement of DAMS and reservoirs to improve the durability of the structure.
Products series
Single textured geomembrane, double-wall textured geomembrane.
Product Specification
* Thickness(mm): 0.30mm~3.00mm
* Width: 4m~8m
* Roll length: 50m~100m (customized request accept)
PS: Customized request accept for all above.
Geomembrane Series
Textured HDPE Geomembrane For Landfill (GB/T 17643-2011(GH-2T1,GH-2T2))
| Serial Number |
Project |
Index |
| Thickness(mm) |
0.75 |
1.00 |
1.25 |
1.50 |
2.00 |
2.50 |
3.00 |
| 1 |
Density (g/c㎡,≥) |
≥0.940 |
| 2 |
Textured Highth (mm) |
≥0.25 |
| 3 |
Yield Strength (N/mm,LD/TD) |
≥11 |
≥15 |
≥18 |
≥22 |
≥29 |
≥37 |
≥44 |
| 4 |
Breaking Strength (N/mm,LD/TD) |
≥8 |
≥10 |
≥13 |
≥16 |
≥21 |
≥26 |
≥32 |
| 5 |
Yeild Elongation Rate (%) |
≥12 |
| 6 |
Breaking Elongation Rate (%) |
≥100 |
| 7 |
Rectangular Tear Strength (N) |
≥93 |
≥125 |
≥160 |
≥190 |
≥250 |
≥315 |
≥375 |
| 8 |
Puncture Strength (N) |
≥200 |
≥270 |
≥335 |
≥400 |
≥535 |
≥670 |
≥800 |
| 9 |
Tensile Load Stress Cracking (Notch Constant Load Tensle Method) h |
≥300 |
| 10 |
Carbon Black Content(Rang) (%) |
2.0~3.0 |
| 11 |
Carbon Black Dispersion |
There is not more than one grade 3 in 10 data, and grade 4 and grade 5 are not allowed |
| 12 |
Oxidative Induction Time (OIT) |
Standard OIT (min)≥100 |
| High Pressure OIT (min)≥400 |
| 13 |
85℃ thermal aging (Atmospheric Pressure OIT Retention After 90 Day) |
≥55 |
| 14 |
Ultraviolet Irradiation After 1600 Hours, The OIT Retention(%) |
≥50 |
|
(CJ-T234-2006)
| Specification |
1.00mm |
1.25mm |
1.50mm |
2.00mm |
2.50mm |
3.00mm |
Remark |
| Item |
| Thickness (mm) |
1.00mm |
1.25mm |
1.50mm |
2.00mm |
2.50mm |
3.00mm |
|
| Textured Highth (mm) |
0.25 |
|
| Density (g/c㎡,≥) |
0.94 |
|
| Tensile Properties |
| Yield Strength (N/mm,LD/TD) |
15 |
18 |
22 |
29 |
37 |
44 |
|
| Breaking Strength (N/mm,LD/TD) |
10 |
13 |
16 |
21 |
26 |
32 |
|
| Yeild Elongation Rate (%) |
12 |
|
| Breaking Elongation Rate (%) |
100 |
|
| Rectangular Tear Strength (N) |
125 |
156 |
187 |
249 |
311 |
374 |
|
| Puncture Strength (N) |
267 |
333 |
400 |
534 |
667 |
800 |
|
Environmental Stress Crack Resistance (h)
(A single point of incision constant tensile method) |
300 |
|
| Carbon Black |
| Carbon Black Content(Rang) (%) |
2.0~3.0 |
|
| Carbon Black Dispersion |
Nine of 10 observation area should be grade 1 or grade 2, not more than 1 of grade3 |
|
| Oxidative Induction Time (OIT) |
| Standard OIT (min) |
100 |
|
| High Pressure OIT (min) |
400 |
|
| 85℃ Oven Ageing (Minimum Average) |
| 90 days after baking, the standard OIT retention(%) |
55 |
|
| 90 days after baking, the hight pressure OIT retention(%) |
80 |
|
| The Anti-UV Strength |
| Ultraviolet irradiation after 1600 hours, the standard OIT retention(%) |
50 |
|
| Ultraviolet irradiation after 1600 hours, the high pressure OIT retention(%) |
50 |
|
| -70℃ The Low Temperature Embrittlement Performance mpact |
Pass |
|
| Water Vapor Penetration Coefficient g.cm (cm2.s.Pa) |
≤1.0X10-13 |
|
| Dimensional Stability |
±2 |
|